https://www.repositorio.mar.mil.br/handle/ripcmb/846413| Título: | Efeitos da adição de nanotubos de carbono de parede simples nas propriedades mecânicas de compósitos de fibra de carbono/epóxi |
| Autor(es): | Costa, Rafael Leal da |
| Orientador(es): | Gondim de Andrade e Silva, Leonardo |
| Palavras-chave: | nanotubos de carbono compósito hierárquico enrolamento filamentar compósito de fibra de carbono nanocompósitos resina epóxi fibra de carbono Carbon nanotubes hierarchical composite filament winding carbon fiber composite nanocomposites epoxy resin carbon fiber |
| Áreas de conhecimento da DGPM: | Engenharia nuclear |
| Data do documento: | 2023 |
| Editor: | Instituto de Pesquisas Energéticas e Nucleares (IPEN) |
| Descrição: | Foi desenvolvido um roteiro de fabricação de compósito hierárquico de matriz epoxy e reforços de fibra de carbono e nanotubos de carbono de paredes únicas. Buscou-se utilizar insumos acessíveis e de fácil aquisição, além de minimizar a complexidade e o número de etapas de fabricação do processo, para que o roteiro seja facilmente implementável em grande escala. Desenvolveu-se um roteiro utilizando um produto comercial composto de uma mistura de nanotubos com agentes dispersantes, foi utilizado um misturador planetário para dispersão do produto na resina em uma única etapa e as placas de compósito foram produzidas por enrolamento filamentar. Os ensaios de flexão mostraram uma melhoria de mais de 10% na resistência à flexão com adição de 87 ppm de nanotubos, além disso a dispersão se mostrou de boa qualidade, ao ser avaliada por microscopia eletrônica de varredura e outros métodos. |
| Abstract: | A fabrication protocol for a hierarchical composite consisting of an epoxy matrix reinforced with carbon fibers and single-walled carbon nanotubes was developed. The aim was to use readily available and easily procured materials while minimizing the complexity and number of fabrication stages, so that the protocol can be easily scaled up. A procedure was developed using a commercial product composed of a mixture of nanotubes with dispersing agents. A planetary mixer was used to disperse the product into the resin in a single step, and the composite plates were produced via filament winding. Flexural tests indicated an improvement of over 10% in flexural strength with the addition of 87 ppm of nanotubes. Furthermore, the dispersion quality was found to be high, as assessed by scanning electron microscopy and other methods. |
| Tipo de Acesso: | Acesso aberto |
| URI: | https://www.repositorio.mar.mil.br/handle/ripcmb/846413 |
| Tipo: | Dissertação |
| Aparece nas coleções: | Engenharia Naval: Coleção de Dissertações |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| Costa - Dissertação de Mestrado v19OUT23.pdf | Efeitos da adição de nanotubos de carbono de parede simples nas propriedades mecânicas de compósitos de fibra de carbono/epóxi | 5,85 MB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.